Sisan ilana
1.Anodizing ti awọn ohun elo ti o da lori fadaka ati awọn ohun elo electrophoretic orisun fadaka: Loading - Rinsing Omi - Ipara-iwọn otutu-iṣan omi - Omi omi ti npa omi - Fifọ - Anodizing - Omi rinsing - Omi rinsing - Omi rinsing - Awọn ihò lilẹ - Omi rinsing Rirọ omi - Blanking - Air gbigbe - Ayẹwo - Titẹsi ilana electrophoresis - Iṣakojọpọ.
2.Anodizing ti awọn ohun elo ti o tutu ati awọn ohun elo electrophoretic frosted: Loading - Degreasing - Water rinsing - Acid etching - Water rinsing - Water rinsing - Alkali etching - Water rinsing - Water rinsing - Neutralization and brightening - Water rinsing - Water rinsing - Clamping - Anodizing Ṣiṣan omi-omi-omi-omi-omi-omi-omi-omi-omi-omi-omi-mimu-mimu-mimu-mimu-omi-omi-omi-omi-omi-omi-omi-afẹfẹ-gbigbẹ-ayẹwo-Titẹ sii ilana electrophoresis - Iṣakojọpọ.
3.Anodizing ti awọn ohun elo ti o ni awọ ati awọn ohun elo eleto-awọ: Loading - Rinsing Water - Irẹwẹsi kekere-iwọn otutu - Igbẹhin omi - Omi rinsing - Clamping - Anodizing - Omi rinsing - Omi rinsing - Omi rinsing - Colouring - Omi rinsing - Omi rinsing - Igbẹhin ihò - Ṣiṣan omi omi - Ṣiṣan omi - Ṣiṣayẹwo - Titẹsi ilana electrophoresis - Blanking - Gbigbe afẹfẹ - Ayẹwo - Iṣakojọpọ.
Anodizing awọn ọja ti MAT Aluminiomu
Nkojọpọ ohun elo
1.Before loading awọn profaili, awọn aaye olubasọrọ ti awọn ọpa gbigbe yẹ ki o wa ni didan ti o mọ, ati awọn ikojọpọ yẹ ki o ṣee ṣe gẹgẹbi nọmba idiwọn. Ilana iṣiro jẹ bi atẹle: Nọmba awọn profaili ti kojọpọ = Iwọn iwuwo lọwọlọwọ lọwọlọwọ x agbegbe profaili ẹyọkan.
2.Principles fun considering awọn nọmba ti awọn agbeko: Iwọn lilo ti agbara ẹrọ silikoni ko yẹ ki o kọja 95%; iwuwo lọwọlọwọ yẹ ki o ṣeto ni 1.0-1.2 A / dm; apẹrẹ profaili yẹ ki o fi awọn aaye pataki silẹ laarin awọn profaili meji.
3.Cacululation of anodizing time: Anodizing time (t) = Film sisanra ibakan K x Lọwọlọwọ iwuwo k, ibi ti K ni awọn electrolysis ibakan, ya bi 0.26-0.32, ati t jẹ ni iṣẹju.
4.Nigbati o ba n gbe awọn agbeko oke, nọmba awọn profaili yẹ ki o tẹle tabili "Agbegbe Profaili ati Nọmba ti Awọn agbeko oke".
5.Lati dẹrọ omi bibajẹ ati gaasi idominugere, awọn agbeko oke yẹ ki o wa ni tilted nigba bundling, pẹlu ohun ti tẹri igun ti ni ayika 5 iwọn.
6.The conductive ọpá le fa kọja awọn profaili nipa 10-20mm lori mejeji opin, ṣugbọn o yẹ ki o ko koja 50mm.
Ilana didan iwọn otutu kekere
1.The fojusi ti kekere-otutu polishing oluranlowo ni ojò yẹ ki o wa ni akoso ni a lapapọ acid fojusi ti 25-30 g / l, pẹlu kan kere ti 15 g / l.
2.The otutu ti awọn polishing ojò yẹ ki o wa ni muduro ni 20-30 ° C, pẹlu kan kere ti 20 ° C. Akoko didan yẹ ki o jẹ awọn aaya 90-200.
3.After gbígbé ati fifa omi ti o ku, awọn profaili yẹ ki o wa ni kiakia ti o ti gbe lọ si omi ti omi fun omi ṣan. Lẹhin omi ṣan omi meji, wọn yẹ ki o gbe wọn lọ ni kiakia si ojò anodizing. Akoko ibugbe ninu ojò omi ko yẹ ki o kọja awọn iṣẹju 3.
4.Before polishing, awọn ohun elo didan iwọn otutu ko yẹ ki o ṣe itọju eyikeyi miiran, ati awọn omi omi omi miiran ko yẹ ki o ṣe sinu ojò didan.
Ilana Ilọkuro
1.Awọn ilana ti npajẹ ni a ṣe ni ojutu acid ni iwọn otutu yara, pẹlu iye akoko 2-4 iṣẹju ati ifọkansi H2SO4 ti 140-160 g / l.
2.After gbígbé ati fifa omi ti o ku, awọn profaili yẹ ki o wa ni gbe sinu omi ojò fun rinsing fun 1-2 iṣẹju.
Frosting (Acid Etching) Ilana
1.After degreasing, awọn profaili yẹ ki o wa ni omi ṣan ni omi omi ṣaaju ki o to wọ inu ojò etching acid.
2.Process paramita: NH4HF4 fojusi ti 30-35 g / l, otutu ti 35-40 ° C, pH iye ti 2.8-3.2, ati acid etching akoko ti 3-5 iṣẹju.
3.After acid etching, awọn profaili yẹ ki o lọ nipasẹ meji omi rinses ṣaaju ki o to titẹ awọn alkali etching ojò.
Alkali Etching Ilana
1.Process paramita: Free NaOH fojusi ti 30-45 g / l, lapapọ alkali fojusi ti 50-60 g / l, alkali etching oluranlowo ti 5-10 g / l, AL3 + fojusi ti 0-15 g / l, otutu ti 35-45 ° C, ati akoko etching alkali fun awọn ohun elo iyanrin ti 30-60 awọn aaya.
2.After gbígbé ati fifa ojutu, awọn profaili yẹ ki o wa ni kiakia ti o ti gbe lọ si omi omi kan fun fifọ ni kikun.
3.The dada didara yẹ ki o wa ni ẹnikeji lẹhin ninu lati rii daju nibẹ ni o wa ti ko si ipata ami, impurities, tabi dada adhesion ṣaaju ki o to titẹ awọn imọlẹ ilana.
Ilana Imọlẹ
1.Process paramita: H2SO4 fojusi ti 160-220 g / l, HNO3 ni o yẹ iye tabi 50-100 g / l, yara otutu, ati imọlẹ akoko ti 2-4 iṣẹju.
2.After gbigbe ati fifa omi ti o ku, awọn profaili yẹ ki o wa ni kiakia ti o ti gbe lọ si omi omi fun awọn iṣẹju 1-2, ti o tẹle omi keji fun awọn iṣẹju 1-2 miiran.
3.After awọn iyipo meji ti mimọ, okun waya aluminiomu lori awọn agbeko yẹ ki o wa ni wiwọ ni wiwọ lati rii daju pe olubasọrọ to dara nigba ilana anodizing. Awọn ohun elo deede ti wa ni dimole ni opin kan ti okun waya aluminiomu agbeko, lakoko ti awọn ohun elo awọ ati awọn ohun elo elekitiroti ti wa ni dimole ni awọn opin mejeeji.
Ilana Anodizing
1.Process paramita: H2SO4 fojusi ti 160-175 g / l, AL3 + fojusi ≤20 g / l, lọwọlọwọ iwuwo ti 1-1.5 A / dm, foliteji ti 12-16V, anodizing ojò otutu ti 18-22 ° C. Awọn electrification akoko ti wa ni iṣiro lilo awọn agbekalẹ. awọn ibeere fiimu anodized: ohun elo fadaka 3-4μm, iyanrin funfun 4-5μm, electrophoresis 7-9μm;
2.Awọn agbeko anode yẹ ki o gbe ni imurasilẹ ni awọn ijoko adaṣe, ati pe o yẹ ki o jẹrisi pe ko si olubasọrọ laarin awọn profaili ati awo cathode ṣaaju ki o to bẹrẹ ilana anodizing.
3.After anodizing, awọn ọpa anode yẹ ki o gbe jade kuro ninu omi, tilted, ati fifa omi ti o ku. Lẹhinna wọn yẹ ki o gbe lọ si ojò omi fun omi ṣan fun awọn iṣẹju 2.
4.Non-coloring profaili le tẹ awọn Atẹle omi ojò fun lilẹ itọju.
Ilana awọ
Awọn ọja 1.Coloring yẹ ki o wa ni idayatọ nikan ni awọn atunto ila-ila-ila kan, pẹlu aaye laarin awọn ọja ti o dọgba si tabi tobi ju iwọn oju ti o baamu ti awọn ọja ti o wa nitosi. Ni gbogbogbo, nigbati a ba wọn nipasẹ awọn ika ọwọ, aaye yẹ ki o tobi ju tabi dọgba si iwọn ika ika meji. Awọn edidi gbọdọ jẹ wiwọ ati aabo, ati pe awọn ila tuntun nikan ni o yẹ ki o lo fun sisọpọ.
2.The anodizing ojò otutu nigba kikun yẹ ki o wa ni akoso ni 18-22 ° C lati rii daju aṣọ ati itanran anodized fiimu sisanra.
3.Awọn agbegbe awọ anodized ni ori ila kọọkan yẹ ki o jẹ to dogba.
4.After coloring, awọn profaili yẹ ki o wa ni tilted, akawe pẹlu kan awọ ọkọ, ati ti o ba awọn ipo ti wa ni pade, won le wa ni rinsed ni kan omi ojò. Bibẹẹkọ, awọn igbese kan pato yẹ ki o mu.
5.O ni imọran lati yago fun awọ awọn oriṣiriṣi awọn ọja tabi awọn ipele ti awọn ọja lori agbeko kanna.
Anodizing awọn ọja ti MAT Aluminiomu
Lilẹ ilana,
1.Place awọn anodized profaili ni a lilẹ ojò lati pa awọn la kọja anodized fiimu ati ki o mu awọn ipata resistance ti awọn anodized fiimu.
2.Process paramita: Deede lilẹ otutu ti 10-30 ° C, lilẹ akoko ti 3-10 iṣẹju, pH iye ti 5.5-6.5, lilẹ oluranlowo fojusi ti 5-8 g / l, nickel ion fojusi ti 0.8-1.3 g / l, ati ifọkansi ion fluoride ti 0.35-0.8 g / l.
3.After lilẹ, gbe awọn agbeko soke, tẹ ki o si fa omi ti o npa omi, gbe wọn lọ si omi omi fun omi ṣan keji (1 iṣẹju ni akoko kọọkan), fifun awọn profaili gbẹ, yọ wọn kuro ninu awọn agbeko, ṣayẹwo ati ki o gbẹ wọn ṣaaju ki o to apoti. .
Ṣatunkọ nipasẹ May Jiang lati MAT Aluminiomu
Akoko ifiweranṣẹ: Oṣu Kẹwa-21-2023